High Alumina Cement
High alumina cement refers to a fast-hardening, high-strength, heat-resistant and corrosion-resistant cementitious material. All clinker based on calcium aluminate and alumina content of about 50% and ground hydraulic cementitious material are called high alumina cement.
Before, the High Alumina Cement is called bauxite cement, which is a kind of grinding hydraulic cementing materials with clinker about 50% Al2O3 content and has calcium aluminate as the main material, which is also called refractory cement, which can be made to low cement high alumina castable to build or repair all kinds of furnace and kilns for thermal insulation or acid erosion resistance with high strength.
The refractory cement in RS Refractory Group uses bauxite and lime as the raw materials, which is a kind of hydraulic binders with aluminate as the main mineral composition that through calcining and grinding fine according to certain proportion. Also known as the professional name Aluminate Cement.
RS Kiln Refractory Manufacturer as one of the professional refractory cement suppliers manufactures all kind of refractory cement for various furnaces and kilns building to resist sulfate attack.
Physical and Chemical Indexes of High Alumina Cement
Product
CA-65
CA-68
CA-70
CA-75
CA-80
Chemical Composition (%)
Al2O3
64-66
67-69
69-71
73-75
77-80
CaO
32-34
29-31
27-29
23-25
18-20
SiO2
1.8
1.2
0.3
0.3
0.3
Fe2O3
0.6
0.6
0.3
0.3
0.3
Specific Surface (cm2/g)
4500
4500
5000
5500
7000
Setting time (h:min)
Initial setting (min)
0:40
0:40
0:40
0:45
0:45
Final Setting (min)
8:00
8:00
10:00
10:00
10:00
Cold Modulus of Rupture (MPa)
24 hour
6.0min
6.0min
6.0min
6.0min
5.0min
72 hour
8.0min
8.0min
8.0min
8.0min
6.0min
Cold Crushing Strength (Mpa)
24hour
45.0min
45.0min
45.0min
45.0min
35.0min
72hour
70.0min
70.0min
70.0min
70.0min
60.0min
Refractoriness (°C)
1680
1710
1730
1750
1770
Properties of High Alumina Cement
Early Strength Characteristics: Its early strength increase rate is far more than rapid hardening portland cement, the high alumina refractory cement is suitable for emergency repair engineering. Take restrictions on the use in structure engineering to prevent from the long-term strength reducing.
Larger Heat of Hydration: Early cement hardening heat release is larger. Compared with Portland cement at same grade, just a day can release 70 ~ 80% of the total heat of hydration. Due to the several kinds of heat release, It is usually be used for low temperature curing of concrete engineering.
Strong Resistance to Sulfate Attack: hydration process generates aluminium hydroxide gel to form a protective film instead of non-precipitating free alternating current calcium hydroxide. Therefore, in the crystal transformation in the process of the erosion resistance will decrease.
Good High Temperature Resistance: This aluminate cement can be used as heat resistant concrete cementitious materials to be configured to heat resistant concrete.
Application of High Alumina Cement
For the configuring of the refractory castable, the refractory cement is main raw materials, such as high alumina low cement castable which can build or repair furnace lining or kiln for heat insulation or high temperature erosion furnaces’ refractory layers.
The cement refractory grade is tested compressive strength of 3 days according to the strength testing method of standard provisions and is divided into four grades of 425, 525, 625 and 725. (According to the GB201-2000 requirement, the cement standard is revised as aluminate cement, aluminate cement standard of division is aluminum content, of which the original series of CA50 is canceled, and set up in accordance with the 3 day strength subdivided such as A600 and A700, A900 grade and etc.)
Fineness
Residue on sieve of 0.088 mm square hole sieve should be less than 10%.
Note: uses specific surface area to replace cement fineness. Specific surface area shall not be less than 2400cm/2g according to GB 207-63 “cement specific surface area testing method”. It subjects to sieve analysis method.
Setting time
Initial high alumina cement setting time should not be earlier than 40 minutes and final setting time should not be later than 10 hours.
Intensity
28 days intensity should be detected and its value shall not be less than grade index for 3 days.
Various cheap high alumina cement for sale in RS Kiln Refractory Materials For Sale Manufacturer. With high quality for high heat equipment refractory lining application, such as refractory cement, low cement high alumina castable, high alumina refractory catable and etc.